Analisi statistica delle proprietà tensili di materiali metallici al variare della temperatura

A methodology was developed to determine a common trend in the variation with temperature of the tensile properties relating to different alloy. For this purpose several parameters, combinations of the main variables obtained from tensile tests, were introduced and analysed as a function of temperature, using both linear and logarithmic scales. The resulting trends were fitted with linear and parabolic regressions. The data used, relating to 270 materials, come mainly from manufacturers; these data were grouped in classes, according to the main element in the alloy. The overall accuracy of the several regressions performed was evaluated by means of suitable variables. Two parameters - depending from Young's modulus, yield strength and UTS values - were determined; their trends with temperature are quantitatively similar for every material of a specific class. È stata sviluppata una metodologia per determinare possibili andamenti comuni nelle variazioni con la temperatura delle proprietà tensili di leghe diverse. A questo scopo sono stati introdotti vari parametri, combinazioni delle principali variabili ottenute da una prova di trazione, e ne è stata analizzata la loro variazione in funzione della temperatura, interpolandone gli andamenti con leggi di tipo lineare e parabolico in scala sia lineare che logaritmica. I dati utilizzati (provenienti in maggior parte direttamente dalle aziende produttrici) sono relativi a 270 materiali, suddivisi in classi in base al principale elemento in lega. Utilizzando opportuni criteri che consentono di poter stimare l’accuratezza complessiva di molteplici regressioni, sono stati determinati due parametri, dipendenti dal modulo di Young e dai carichi di snervamento e di rottura, i cui andamenti in funzione della temperatura risultano quantitativamente simili per tutti i materiali di una determinata classe.