Multilevel fatigue from life prediction methods

A life prediction method has been used to compute the life of a given alloy in conditions of multilevel fatigue. The effect of the order of the loads has been verified for two levels and repeated blocks of them. In case of two levels, a double linear scheme was obtained with the demarcation point depending upon the completion of the nucleation stage. In case of successive blocks at two levels the results depend on the selected life fraction values: for large LF the two-level limit is approached; for small LF and many blocks in succession, the order becomes indifferent and the favourable combination leading to total life greater than one can no longer be observed. Viene utilizzato un modello di previsione per calcolare la vita di una lega di Ni in condizioni di fatica a più livelli di sollecitazione. L'effetto dell'ordine dei valori di carico è stato determinato per due livelli, ottenendo un comportamento bi-lineare. Per blocchi di due livelli ripetuti fino a rottura, il comportamento dipende fortemente dai valori della frazione di vita che in un blocco vengono spesi a ciascun livello: l'effetto di ordine è trascurabile con frazioni di vita piccole e aumenta, fino a limite rappresentato dal caso di un solo blocco, via via che i valori delle frazioni di vita aumentano.