In the framework of high-temperature low-cycle fatigue, a specific problem concerns the correct evaluation of creep and fatigue contributions to total life. In this work, specimens of IN 738 and IN 792 have been fatigue tested at high temperature. Particular attention has been given to the application to the test results of life prediction methods. A multistage model has been used. After fitting the model to the particular alloy, fatigue maps can be derived and life prediction can be extended to multilevel tests. A complete set of predictions can thus been obtained which provides information on the general mechanical behaviour of the material. Sono riportati i risultati di un'indagine sulla resistenza meccanica ad alta temperatura di due superleghe di Ni per palette di turbine. Dopo aver descritto l'apparato sperimentale per la realizzazione delle prove, sono presentati e discussi i risultati di prove di stress rupture e di fatica oligociclica condotte a due temperature. Le prove meccaniche sono affiancate da sistematiche indagini frattografiche. I dati sono soddisfacentemente interpretati con un modello di previsione di vita, che viene quindi utilizzato per ottenere informazioni sul comportamento meccanico generale dei materiali in esame.
Fatigue life prediction and verification for superalloys / A.Del Puglia; F.Pratesi; G.Zonfrillo; M.Becagli. - STAMPA. - II:(1990), pp. 1107-1119. (Intervento presentato al convegno High Temperature Materials for Power Engineering 1990 tenutosi a Liegi (Belgio) nel 24-27 September 1990).
Fatigue life prediction and verification for superalloys
DEL PUGLIA, ALDO;PRATESI, FRANCO;ZONFRILLO, GIOVANNI;
1990
Abstract
In the framework of high-temperature low-cycle fatigue, a specific problem concerns the correct evaluation of creep and fatigue contributions to total life. In this work, specimens of IN 738 and IN 792 have been fatigue tested at high temperature. Particular attention has been given to the application to the test results of life prediction methods. A multistage model has been used. After fitting the model to the particular alloy, fatigue maps can be derived and life prediction can be extended to multilevel tests. A complete set of predictions can thus been obtained which provides information on the general mechanical behaviour of the material. Sono riportati i risultati di un'indagine sulla resistenza meccanica ad alta temperatura di due superleghe di Ni per palette di turbine. Dopo aver descritto l'apparato sperimentale per la realizzazione delle prove, sono presentati e discussi i risultati di prove di stress rupture e di fatica oligociclica condotte a due temperature. Le prove meccaniche sono affiancate da sistematiche indagini frattografiche. I dati sono soddisfacentemente interpretati con un modello di previsione di vita, che viene quindi utilizzato per ottenere informazioni sul comportamento meccanico generale dei materiali in esame.I documenti in FLORE sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.