A set of HTLCF tests is reported for a IN 792 DS superalloy containing hafnium. Two different kinds of fracture are observed. The first occurs in the central zone of the test-bar with a propagation perpendicular to the tension axis, and is similar to that already observed in other specimens of the same alloy. The second occurs near the neck of the test-bar, where temperature is lower; one of its characteristics is that a significant part of propagation is found along crystal planes oriented at about 45°. Possible causes of this behaviour are experimentally investigated by means of specific tests. The conclusion is that an interpretation of experimental results requires the presence in the test section of both a physical-metallurgical factor and a factor connected to the actual stresses. Sono presentati e discussi risultati di prove HTLCF condotte sulla superlega IN 792 DS contenente afnio. Sono state osservate due modalità di rottura. La prima avviene nella zona centrale del provino con propagazione ortogonale all'asse del carico, ed è simile a quella osservata in prove precedentemente condotte su diversi campioni della stessa lega. La seconda si verifica presso il raccordo del provino, dove la temperatura è più bassa ed è caratterizzata dal fatto è che una parte significativa della propagazione avviene lungo piani cristallografici orientati a circa 45°. Specifiche prove sono condotte per verificare le principali cause che determinano tale comportamento del materiale. Si conclude che l'interpretazione dell'insieme dei risultati richiede sia un fattore fisico-metallurgico nella sezione che un fattore relativo alle reali sollecitazioni agenti sul provino.
Modalità di frattura per una superlega solidificata direzionalmente / F.Pratesi; G.Zonfrillo; M.Giannozzi; A.Del Puglia. - STAMPA. - (1993), pp. 39-51. (Intervento presentato al convegno IX Conv. Naz. del Gruppo Italiano Frattura tenutosi a Roma nel 2-4 giugno 1993).
Modalità di frattura per una superlega solidificata direzionalmente
PRATESI, FRANCO;ZONFRILLO, GIOVANNI;DEL PUGLIA, ALDO
1993
Abstract
A set of HTLCF tests is reported for a IN 792 DS superalloy containing hafnium. Two different kinds of fracture are observed. The first occurs in the central zone of the test-bar with a propagation perpendicular to the tension axis, and is similar to that already observed in other specimens of the same alloy. The second occurs near the neck of the test-bar, where temperature is lower; one of its characteristics is that a significant part of propagation is found along crystal planes oriented at about 45°. Possible causes of this behaviour are experimentally investigated by means of specific tests. The conclusion is that an interpretation of experimental results requires the presence in the test section of both a physical-metallurgical factor and a factor connected to the actual stresses. Sono presentati e discussi risultati di prove HTLCF condotte sulla superlega IN 792 DS contenente afnio. Sono state osservate due modalità di rottura. La prima avviene nella zona centrale del provino con propagazione ortogonale all'asse del carico, ed è simile a quella osservata in prove precedentemente condotte su diversi campioni della stessa lega. La seconda si verifica presso il raccordo del provino, dove la temperatura è più bassa ed è caratterizzata dal fatto è che una parte significativa della propagazione avviene lungo piani cristallografici orientati a circa 45°. Specifiche prove sono condotte per verificare le principali cause che determinano tale comportamento del materiale. Si conclude che l'interpretazione dell'insieme dei risultati richiede sia un fattore fisico-metallurgico nella sezione che un fattore relativo alle reali sollecitazioni agenti sul provino.I documenti in FLORE sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.